Reinforcement of water seepage prevention in reservoir HDPE Geomembrane

Product specifications;

Materials; Mainly divided into: low-density polyethylene (LDPE) geomembrane, high-density polyethylene (HDPE) geomembrane, and EVA geomembrane.

Thickness; 1.0-2.0mm

Wide width; 4-8 meters

If there are special requirements, such as packaging requirements (width, length, thickness), please inform customer service personnel

Contact Now E-Mail Telephone WhatsApp

Product Details

Reinforcement of water seepage prevention in reservoir HDPE Geomembrane

With whole specs of width and thickness, it has outstanding resistance to environmental stress cracking and chemical corrosion, as desirable as magnificent resistance to chemical corrosion. It has a massive temperature range and a prolonged issuer life, and is used in landfill sites, tailings storage sites, canal seepage prevention, dam seepage prevention, and subway engineering

Special waterproofing for landfill sites HDPE Geomembrane

Product characteristics;

According to countrywide standards, polyethylene movie with a thickness of 0.2m and a stabilizer used in hydraulic engineering can work for up to 40-50 years beneath smooth water prerequisites and 30-40 years below sewage conditions, relying on whether or not the plastic movie has misplaced its anti-seepage and water blocking off effect. Therefore, the carrier existence of the geomembrane is ample to meet the anti-seepage requirements of the dam.

Reinforcement of water seepage prevention in reservoir HDPE Geomembrane

Application scope;

Environmental protection and hygiene engineering, water conservancy and geotechnical engineering, municipal engineering, landscaping, stone mining, aquaculture industry (fish pond, shrimp pond lining, etc.)

HDPE Geomembrane Technical Parameter (GRI GM13 ASTM Standard)
Spec Properties	Test method ASTM	GMS0.5	GMS0.75	GMS1.0	GMS1.25	GMS1.5	GMS2.0	GMS2.5
Thickness	D5199	0.5mm	0.75mm	1.00mm	1 .25mm	1.50mm	2.00mm	2.50mm
Density (≥ g/cc)	D1505	0.940	0.940	0.940	0.940	0.940	0.940	0.940
Tensile Properties (Each direction)(≥) • yield strength • break strength • yield elongation • break elongation	D6693 Type IV	8 kN/m 14 kN/m 12% 700%	11 kN/m 20 kN/m 12% 700%	15 kN/m 27 kN/m 12% 700%	18 kN/m 33 kN/m 12% 700%	22 kN/m 40 kN/m 12% 700%	29kN/m 53 KN/m 12% 700%	37kN/m 67kN/m 12% 700%
Tear Resistance (≥)	D 1004	64N	93N	125 N	156N	187N	249 N	311 N
Puncture Resistance(≥)	D 4833	160N	240N	320 N	400 N	480N	640 N	800 N
Stress Crack Resistance (≥)	D 5397	300 hr	300 hr	300 hr	300 hr	300 hr	300 hr	300 hr
Carbon Black Content	D 1603	2.0-3.0%	2.0-3.0%	2.0-3.0%	2.0-3.0%	2.0-3.0%	2.0-3.0%	2.0-3.0%
Carbon Black Dispersion	D 5596	Note(1)	Note(1)	Note(1)	Note(1)	Note(1)	Note(1)	Note(1)
Oxidative Induction Time(OIT)(≥) (a)Standard OIT ——or—— (b)High Pressure OIT	D 3895 D 5885	100 min 400 min	100 min 400 min	100 min 400 min	100 min 400 min	100 min 400 min	100 min 400 min	100 min 400 min

Packing of High Quality HDPE Geomembrane Pond Liner

Reinforcement of water seepage prevention in reservoir HDPE Geomembrane

Pond Liner geotextile membrane for water seepage prevention HDPE Geomembrane

Special waterproofing for landfill sites HDPE Geomembrane

Usage Scenarios of High Quality HDPE Geomembrane Pond Liner

Reinforcement of water seepage prevention in reservoir HDPE Geomembrane

HDPE Geomembrane Technical Parameter (GRI GM13 ASTM Standard)
Spec Properties	Test method ASTM	GMS0.5	GMS0.75	GMS1.0	GMS1.25	GMS1.5	GMS2.0	GMS2.5
Thickness	D5199	0.5mm	0.75mm	1.00mm	1 .25mm	1.50mm	2.00mm	2.50mm
Density (≥ g/cc)	D1505	0.940	0.940	0.940	0.940	0.940	0.940	0.940
Tensile Properties (Each direction)(≥) • yield strength • break strength • yield elongation • break elongation	D6693 Type IV	8 kN/m 14 kN/m 12% 700%	11 kN/m 20 kN/m 12% 700%	15 kN/m 27 kN/m 12% 700%	18 kN/m 33 kN/m 12% 700%	22 kN/m 40 kN/m 12% 700%	29kN/m 53 KN/m 12% 700%	37kN/m 67kN/m 12% 700%
Tear Resistance (≥)	D 1004	64N	93N	125 N	156N	187N	249 N	311 N
Puncture Resistance(≥)	D 4833	160N	240N	320 N	400 N	480N	640 N	800 N
Stress Crack Resistance (≥)	D 5397	300 hr	300 hr	300 hr	300 hr	300 hr	300 hr	300 hr
Carbon Black Content	D 1603	2.0-3.0%	2.0-3.0%	2.0-3.0%	2.0-3.0%	2.0-3.0%	2.0-3.0%	2.0-3.0%
Carbon Black Dispersion	D 5596	Note(1)	Note(1)	Note(1)	Note(1)	Note(1)	Note(1)	Note(1)
Oxidative Induction Time(OIT)(≥) (a)Standard OIT ——or—— (b)High Pressure OIT	D 3895 D 5885	100 min 400 min	100 min 400 min	100 min 400 min	100 min 400 min	100 min 400 min	100 min 400 min	100 min 400 min